表征了钛/钢爆炸焊接复合板的界面组织和剪切性能,研究了爆炸复合过程的界面结合机理。结果表明,在金属板之间形成了波状界面组织,剧烈塑性变形造成钢基体发生明显的塑性流动,并在界面形成连续的漩涡特征。TEM和XRD检测证实界面存在纳米尺度的过渡层,并包含有固溶体组织和少量金属间化合物。波状界面组织改善了复合板沿爆炸方向的界面剪切强度,剪切断口显示漩涡组织发生韧性断裂特征。
The microstructural characterization and interracial shear tests of Ti/Steel bimetallic clad sheets were taken to study the interfacial bonding mechanism during the explosive welding process. The results show that the wavy interface with several vortexes forms between the dissimilar metal matrixes due to the interface deformation. A significant metal flow of steel matrix caused by the severe plastic deformation induces the continuous vortexes in the interface. The TEM and XRD analyses clarify that the nanoscale interfacial interlayer contains solid solutions and a small amount of intermetallic compounds. The shear strength of the interface along the explosive welding direction is enhanced by the wavy interface. The fracture of the bonding interface presents the ductile features on the vortex while brittle features on the smooth interface.
出处
《稀有金属材料与工程》
SCIE
EI
CAS
CSCD
北大核心
2017年第4期906-911,共6页
Rare Metal Materials and Engineering
基金
National Natural Science Foundation of China(50971038)
关键词
复合板
爆炸焊接
界面
TEM
金属间化合物
clad sheet
explosive welding
interface
TEM
intermetallic compounds