The dissolution property of high-ferrite gibbsitic bauxite and the effect of ferrite content on the dissolution kinetics of gibbsitic bauxites in sodium hydroxide solution under atmospheric pressure from 50 to 90 °C were systematically investigated.The dissolution property of high-ferrite gibbsitic bauxite is increased by increasing the dissolution temperature and the Na OH concentration or decreasing the particle size of bauxite,which is easy to dissolve under atmospheric pressure.The kinetic equations of gibbsitic bauxites with different ferrite contents during the dissolution process at different temperatures for different times were established,and the corresponding activation energies were calculated.The ferrite in the gibbsitic bauxite reduces the dissolution speed and increases the activation energy of dissolution,the diffusion process of which is the rate-controlling step.
The dissolution property of high-ferrite gibbsitic bauxite and the effect of ferrite content on the dissolution kinetics of gibbsitic bauxites in sodium hydroxide solution under atmospheric pressure from 50 to 90 °C were systematically investigated.The dissolution property of high-ferrite gibbsitic bauxite is increased by increasing the dissolution temperature and the Na OH concentration or decreasing the particle size of bauxite,which is easy to dissolve under atmospheric pressure.The kinetic equations of gibbsitic bauxites with different ferrite contents during the dissolution process at different temperatures for different times were established,and the corresponding activation energies were calculated.The ferrite in the gibbsitic bauxite reduces the dissolution speed and increases the activation energy of dissolution,the diffusion process of which is the rate-controlling step.
作者
杨会宾
潘晓林
于海燕
涂赣峰
孙俊民
YANG Hui-bin PAN Xiao-lin YU Hai-yan TU Gan-feng SUN Jun-min(School of Metallurgy, Northeastern University, Shenyang 110004, China Datang International High Aluminum Coal R&D Center (National Energy Sources High Aluminum Coal Development and Utilization Key Laboratory), Ordos 010321, China)
基金
Projects(51104041,51174054,51374065)supported by the National Natural Science Foundation of China
Project(N130402010)supported by the Fundamental Research Funds for the Central Universities of China