摘要
Dynamic mechanical relaxations of La-based metallic glasses were investigated by mechanical spectroscopy.In the framework of the mixing enthalpy of constituent atoms,it was found thatβrelaxation was less evident by the addition of Cu to replace Ni in the LaCuNiAl glassy alloy.By introducing Cu into the LaNiAl metallic glass,the mixing enthalpy was less negative,which led to weakerβrelaxation of the metallic glasses.Theαrelaxation of the La-based metallic glasses could be described by a Kohlrausch-Williams-Watts(KWW)function with a Kohlrausch exponentβKWW around 0.5.It should be noted that physical aging above the glass transition temperature Tginduced a decrease ofβrelaxation intensity in the La-based metallic glass.
Dynamic mechanical relaxations of La-based metallic glasses were investigated by mechanical spectroscopy.In the framework of the mixing enthalpy of constituent atoms,it was found thatβrelaxation was less evident by the addition of Cu to replace Ni in the LaCuNiAl glassy alloy.By introducing Cu into the LaNiAl metallic glass,the mixing enthalpy was less negative,which led to weakerβrelaxation of the metallic glasses.Theαrelaxation of the La-based metallic glasses could be described by a Kohlrausch-Williams-Watts(KWW)function with a Kohlrausch exponentβKWW around 0.5.It should be noted that physical aging above the glass transition temperature Tginduced a decrease ofβrelaxation intensity in the La-based metallic glass.
基金
supported by National Natural Science Foundation of China(51401192,51611130120and 11572249)
the Natural Science Foundation of Shaanxi Province(No.2016JM5009)
the Aeronautical Science Foundation of China(2015ZF53072)
Opening Fund of State Key Laboratory of Materials Processing and Die&Mould Technology,Huazhong University of Science and Technology(P2016-12)
support from MINECO(FIS2014-54734-P)
Generalitat de Catalunya(2014SGR00581)