The serrated plastic flow,microstructure and residual stress of a Zr_（55）Cu_（30）Ni_5Al_（10） bulk metallic glass（BMG）undergone surface mechanical attrition treatment（SMAT）have been investigated by a combination of compression tests with scanning electron microscopy（SEM）,high resolution transmission electron microscopy（HRTEM）and the incremental hole-drilling strain-gage method.It is found that SMAT leads to various microstructural modifications and residual stress distribution in the surface layers of the Zrbased BMG due to the mechanically-induced nanocrystallization and generation of shear bands.As a result,the BMG alloy exhibits a remarkable work-hardening like behavior and significant increase of plastic strain from less than 1%to 15%,and its plastic deformation dynamics yields a power-law distribution of shear avalanches.Based upon the analysis of the experimental results,it is indicated that this can be connected to the SMAT-induced microstructural modifications and the resulting residual compressive stress in the Zr-based BMG.
The serrated plastic flow,microstructure and residual stress of a Zr_（55）Cu_（30）Ni_5Al_（10） bulk metallic glass（BMG）undergone surface mechanical attrition treatment（SMAT）have been investigated by a combination of compression tests with scanning electron microscopy（SEM）,high resolution transmission electron microscopy（HRTEM）and the incremental hole-drilling strain-gage method.It is found that SMAT leads to various microstructural modifications and residual stress distribution in the surface layers of the Zrbased BMG due to the mechanically-induced nanocrystallization and generation of shear bands.As a result,the BMG alloy exhibits a remarkable work-hardening like behavior and significant increase of plastic strain from less than 1%to 15%,and its plastic deformation dynamics yields a power-law distribution of shear avalanches.Based upon the analysis of the experimental results,it is indicated that this can be connected to the SMAT-induced microstructural modifications and the resulting residual compressive stress in the Zr-based BMG.
基金
the financial supports provided by National Natural Science Foundation of China(Grant Nos.51171099,50871063)
the MOST 973 Program of China(Grant Nos.2015CB856800 and 2012CB932203)