摘要
The high pressure and high temperature（HPHT） method is successfully used to synthesize jadeite in a temperature range of 1000℃–1400℃ under a pressure of 3.5 GPa. The initial raw materials are Na2SiO3·9H2O and Al2（SiO3）3.Through the HPHT method, the amorphous glass material is entirely converted into crystalline jadeite. We can obtain the good-quality jadeite by optimizing the reaction pressure and temperature. The measurements of x-ray diffraction（XRD）,scanning electron microscopy（SEM）, Fourier-transform infrared（FTIR） and Raman scattering indicate that the properties of synthesized jadeite at 1260℃ under 3.5 GPa are extremely similar to those of the natural jadeite. What is more, the results will be valuable for understanding the formation process of natural jadeite. This work also reveals the mechanism for metamorphism of magma in the earth.
The high pressure and high temperature（HPHT） method is successfully used to synthesize jadeite in a temperature range of 1000℃–1400℃ under a pressure of 3.5 GPa. The initial raw materials are Na2SiO3·9H2O and Al2（SiO3）3.Through the HPHT method, the amorphous glass material is entirely converted into crystalline jadeite. We can obtain the good-quality jadeite by optimizing the reaction pressure and temperature. The measurements of x-ray diffraction（XRD）,scanning electron microscopy（SEM）, Fourier-transform infrared（FTIR） and Raman scattering indicate that the properties of synthesized jadeite at 1260℃ under 3.5 GPa are extremely similar to those of the natural jadeite. What is more, the results will be valuable for understanding the formation process of natural jadeite. This work also reveals the mechanism for metamorphism of magma in the earth.
基金
supported by the National Natural Science Foundation of China(Grant Nos.51172089 and 51171070)
the Graduate Innovation Fund of Jilin University,China(Grant No.2016065)