摘要
研究了快淬Nd_(12-x)Sm_xFe_(84)B_6(x=0~12)薄带的磁性能。结果表明:快淬速度为30 m/s,矫顽力和磁化强度都随Sm含量的增加而减少。剩磁比随Sm含量的增加呈现先降后升再降的趋势。由于Sm_2Fe_(14)B的磁晶各向异性低于Nd_2Fe_(14)B,随Sm替代量的增加,Nd_(12-x)Sm_xFe_(84)B_6合金的磁晶各向异性逐渐降低,导致矫顽力逐渐减少。
The magnetic properties of Nd12-xSmxFe84B6 melt-spun ribbons (x=0-12) were investigated. The results show that the coercivity and saturation magnetization both decrease with the increase of Sm content under rapid quenching speed of 30 m/s. The remanence ratio shows the tendency of falling firstly and rising and then falling with the increase of Sm content. Because the magnetocrystaUine anisotropy of Sm2Fe14B is lower than that of Nd2Fe14B ,the magnetocrystalline anisotropy of Nd12-xSmxFe84B6 decreases gradually with the increase of the substitution by Sm,which should be responsible for the decrease of coercivity graduaUy.
出处
《热加工工艺》
CSCD
北大核心
2017年第10期60-62,66,共4页
Hot Working Technology
基金
中国国家重点基础研究项目(973项目
2014CB643703)
国家自然科学基金资助项目(51261004)
广西自然科学基金(2015GXNSFAA139249)
关键词
钕铁硼
钐
快淬薄带
磁性能
Nd2Fe14B
Sm
melt-spun ribbon
magnetic property