摘要
The formation of protective multifunctional coatings on magnesium alloy MA8 using plasma electrolyt- ic oxidation （PEO） in an electrolytic system containing nanosized particles of titanium nitride was investigated. Electrochemical and mechanical properties of the obtained layers were examined. It was established that microhardness of the coating with the nanoparticle concentration of 3 gl-1 increased twofold （4.2 ± 0.5 GPa）, while wear resistance decreased （4.97 × 10-6 mm3 N-1 m-1）, as compared to re- spective values for the PEO-coating formed in the electrolyte without nanoparticles （2.1 ± 0.3 GPa, 1.12 × 10.5 mm3 N-1 m-1）.
The formation of protective multifunctional coatings on magnesium alloy MA8 using plasma electrolyt- ic oxidation （PEO） in an electrolytic system containing nanosized particles of titanium nitride was investigated. Electrochemical and mechanical properties of the obtained layers were examined. It was established that microhardness of the coating with the nanoparticle concentration of 3 gl-1 increased twofold （4.2 ± 0.5 GPa）, while wear resistance decreased （4.97 × 10-6 mm3 N-1 m-1）, as compared to re- spective values for the PEO-coating formed in the electrolyte without nanoparticles （2.1 ± 0.3 GPa, 1.12 × 10.5 mm3 N-1 m-1）.
基金
financially supported by the Russian Science Foundation(Project No.14-33-00009)
the Russian Federation Government(Federal Agency of Scientific Organizations)