The grain refinement and macrosegregation control of GCrl5 bearing steel were investigated under a type of rarely-used electromagnetic stirring, vertical electromagnetic stirring （V-EMS）, in continuous casting. V-EMS can create an upward electromagnetic force and generate longitudinal loop convection, which ena- bles the better mixing of the upper part with the lower part of the liquid steel. The results showed that ap- plying V-EMS can enlarge the region of the equiaxed grain, decrease the secondary dendrite arm spacing （SDAS） and reduce the segregation of both carbon and sulfur. After applying V-EMS, liquid steel with a high solute concentration is brought to the dendrite tips, making the dendrite arms partially melt. The length of the dendrite fragment is approximately 1.8 mm, 10 to 12 times the SDAS. Upon increasing the amount of cooling water from 2.0 to 3.5 m3/h, the dendrite fragments exhibit an obvious aggregation fol- lowing V-EMS. Finally, a criterion for dendrite fragmentation under V-EMS was derived based on the dendrite fragmentation theory of Campanella et al.
The grain refinement and macrosegregation control of GCrl5 bearing steel were investigated under a type of rarely-used electromagnetic stirring, vertical electromagnetic stirring （V-EMS）, in continuous casting. V-EMS can create an upward electromagnetic force and generate longitudinal loop convection, which ena- bles the better mixing of the upper part with the lower part of the liquid steel. The results showed that ap- plying V-EMS can enlarge the region of the equiaxed grain, decrease the secondary dendrite arm spacing （SDAS） and reduce the segregation of both carbon and sulfur. After applying V-EMS, liquid steel with a high solute concentration is brought to the dendrite tips, making the dendrite arms partially melt. The length of the dendrite fragment is approximately 1.8 mm, 10 to 12 times the SDAS. Upon increasing the amount of cooling water from 2.0 to 3.5 m3/h, the dendrite fragments exhibit an obvious aggregation fol- lowing V-EMS. Finally, a criterion for dendrite fragmentation under V-EMS was derived based on the dendrite fragmentation theory of Campanella et al.
基金
supported by the National Natural Science Foundation of China(No.50834009)
the Key Project of the Ministry of Education of China(No.311014)
the 111 Project of China(No.B07015)