Combined with the advantages of low melting point,high thermal stability and strong acidity,a multipleSO_3H functioned ionic liquid(MIL) was developed successfully as a curing agent to promote the curing reaction of phthalonitrile-terminated poly(phthalazinone ether nitrile)(PPEN-Ph).The curing kinetics over differential scanning calorimetry(DSC) showed that both the initial curing temperature Tp0' and apparent activation energy Ea'(based on Kissinger equation) were reduced significantly over MIL(207.9℃ and 101.5 kJ/mol) compared to the common curing agent ZnCl_2(268.5℃ and 201.5 kJ/mol).Moreover,under identical curing conditions,the resulting thermosetting resin over former(Td5%=526.1℃) showed better thermal stability than that over latter(Td5%=512.1 ℃).These results indicated that MIL should be a good candidate as a curing agent for phthalonitrile resins.
Combined with the advantages of low melting point,high thermal stability and strong acidity,a multipleSO_3H functioned ionic liquid(MIL) was developed successfully as a curing agent to promote the curing reaction of phthalonitrile-terminated poly(phthalazinone ether nitrile)(PPEN-Ph).The curing kinetics over differential scanning calorimetry(DSC) showed that both the initial curing temperature Tp0' and apparent activation energy Ea'(based on Kissinger equation) were reduced significantly over MIL(207.9℃ and 101.5 kJ/mol) compared to the common curing agent ZnCl_2(268.5℃ and 201.5 kJ/mol).Moreover,under identical curing conditions,the resulting thermosetting resin over former(Td5%=526.1℃) showed better thermal stability than that over latter(Td5%=512.1 ℃).These results indicated that MIL should be a good candidate as a curing agent for phthalonitrile resins.
基金
supported by National Natural Science Foundation of China(No.51273029)
the Fundamental Research Funds for the Central Universities(No.DUT15RC(3)032)
General Project of Scientific Research of the Education Department of Liaoning Province(No.L2015116)
a collaborative project from Guangdong Provincial Key Laboratory of Mineral Physics and Materials(No.GLMPM-010)