摘要
A series of MgO-based adsorbents were prepared through solution–combustion synthesis and ball-milling process.The prepared MgO-based powders were characterized using X-ray diffraction,scanning electron microscopy,N_2 physisorption measurements,and employed as potential adsorbents for CO_2 adsorption.The influence of structural and textural properties of these adsorbents over the CO_2 adsorption behaviour was also investigated.The results showed that MgO-based products prepared by solution–combustion and ball-milling processes,were highly porous,fluffy,nanocrystalline structures in nature,which are unique physico-chemical properties that significantly contribute to enhance their CO_2 adsorption.It was found that the MgO synthesized by solution combustion process,using a molar ratio of urea to magnesium nitrate（2：1）,and treated by ball-milling during 2.5 hr（MgO-BM2.5h）,exhibited the maximum CO_2 adsorption capacity of 1.611 mmol/g at 25℃ and 1 atm,mainly via chemisorption.The CO_2 adsorption behaviour on the MgO-based adsorbents was correlated to their improved specific surface area,total pore volume,pore size distribution and crystallinity.The reusability of synthesized MgO-BM2.5h was confirmed by five consecutive CO_2adsorption–desorption times,without any significant loss of performance,that supports the potential of MgO-based adsorbent.The results confirmed that the special features of MgO prepared by solution–combustion and treated by ball-milling during 2.5 hr are favorable to be used as effective MgO-based adsorbent in post-combustion CO_2 capture technologies.
A series of MgO-based adsorbents were prepared through solution–combustion synthesis and ball-milling process.The prepared MgO-based powders were characterized using X-ray diffraction,scanning electron microscopy,N_2 physisorption measurements,and employed as potential adsorbents for CO_2 adsorption.The influence of structural and textural properties of these adsorbents over the CO_2 adsorption behaviour was also investigated.The results showed that MgO-based products prepared by solution–combustion and ball-milling processes,were highly porous,fluffy,nanocrystalline structures in nature,which are unique physico-chemical properties that significantly contribute to enhance their CO_2 adsorption.It was found that the MgO synthesized by solution combustion process,using a molar ratio of urea to magnesium nitrate（2：1）,and treated by ball-milling during 2.5 hr（MgO-BM2.5h）,exhibited the maximum CO_2 adsorption capacity of 1.611 mmol/g at 25℃ and 1 atm,mainly via chemisorption.The CO_2 adsorption behaviour on the MgO-based adsorbents was correlated to their improved specific surface area,total pore volume,pore size distribution and crystallinity.The reusability of synthesized MgO-BM2.5h was confirmed by five consecutive CO_2adsorption–desorption times,without any significant loss of performance,that supports the potential of MgO-based adsorbent.The results confirmed that the special features of MgO prepared by solution–combustion and treated by ball-milling during 2.5 hr are favorable to be used as effective MgO-based adsorbent in post-combustion CO_2 capture technologies.
基金
the National Institute of Nuclear Research(ININ),México,for financial support through project CB-406 stagesⅠ-Ⅲ