The microstructures and mechanical properties of ferrite-based lightweight steel with different compositions were investigated by tensile test,scanning electron microscopy（SEM）,transmission electron microscopy（TEM）,X-ray diffraction（XRD）and thermodynamic calculation（TC）.It was shown that the ferrite-based lightweight steels with 5wt.%or 8wt.%Al were basically composed of ferrite,austenite andκ-carbide.As the annealing temperature increased,the content of the austenite in the steel gradually increased,while theκ-carbide gradually decomposed and finally disappeared.The mechanical properties of the steel with 5wt.%Al and 2wt.%Cr,composed of ferrite and Cr7C3carbide at different annealing temperatures,were significantly inferior to those of others.The steel containing 5wt.%Al,annealed at 820°C for 50sthen rapidly cooled to 400°C and held for 180s,can obtain the best product of strength and elongation（PSE）of 31242MPa·%.The austenite stability of the steel is better,and its PSE is higher.In addition,the steel with higher PSE has a more stable instantaneous strain hardening exponent（n value）,which is mainly caused by the effect of transformation induced plasticity（TRIP）.When theκ-carbide or Cr7C3carbide existed in the microstructure of the steel,there was an obvious yield plateau in the tensile curve,while its PSE decreased significantly.
The microstructures and mechanical properties of ferrite-based lightweight steel with different compositions were investigated by tensile test,scanning electron microscopy（SEM）,transmission electron microscopy（TEM）,X-ray diffraction（XRD）and thermodynamic calculation（TC）.It was shown that the ferrite-based lightweight steels with 5wt.%or 8wt.%Al were basically composed of ferrite,austenite andκ-carbide.As the annealing temperature increased,the content of the austenite in the steel gradually increased,while theκ-carbide gradually decomposed and finally disappeared.The mechanical properties of the steel with 5wt.%Al and 2wt.%Cr,composed of ferrite and Cr7C3carbide at different annealing temperatures,were significantly inferior to those of others.The steel containing 5wt.%Al,annealed at 820°C for 50sthen rapidly cooled to 400°C and held for 180s,can obtain the best product of strength and elongation（PSE）of 31242MPa·%.The austenite stability of the steel is better,and its PSE is higher.In addition,the steel with higher PSE has a more stable instantaneous strain hardening exponent（n value）,which is mainly caused by the effect of transformation induced plasticity（TRIP）.When theκ-carbide or Cr7C3carbide existed in the microstructure of the steel,there was an obvious yield plateau in the tensile curve,while its PSE decreased significantly.
基金
supported by the Shanghai Municipal Natural Science Foundation(Grant No.17ZR1410400)
the Shanghai Municipal Science and Technology Commission(Grant Nos.15DZ2260300,15DZ2260301)