Twin boundaries（TBs） are key factors influencing the mechanical properties of crystalline materials. We have investigated the intrinsic fatigue cracking mechanisms of TBs during the past decade. The effects of TB orientations on the fatigue cracking mechanisms were revealed via cyclic deformation of a series of grown Cu bicrystals with a sole TB. Furthermore, the combined effects of crystallographic orientation and stacking fault energy（SFE） on the fatigue cracking mechanisms were clarified through cyclic deformation of polycrystalline Cu and Cu alloys. Both developments were reviewed in this report which will provide implications to optimize the interfacial design for the improvement of fatigue performance of metallic materials.
Twin boundaries（TBs） are key factors influencing the mechanical properties of crystalline materials. We have investigated the intrinsic fatigue cracking mechanisms of TBs during the past decade. The effects of TB orientations on the fatigue cracking mechanisms were revealed via cyclic deformation of a series of grown Cu bicrystals with a sole TB. Furthermore, the combined effects of crystallographic orientation and stacking fault energy（SFE） on the fatigue cracking mechanisms were clarified through cyclic deformation of polycrystalline Cu and Cu alloys. Both developments were reviewed in this report which will provide implications to optimize the interfacial design for the improvement of fatigue performance of metallic materials.
作者
Zhefeng Zhang
Linlin Li
Zhenjun Zhang
Peng Zhang
Zhefeng Zhang Linlin Li Zhenjun Zhang Peng Zhang(Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China)
基金
supported by the National Natural Science Foundation of China (NSFC) under Grant Nos. 51471170, 51501197 and 51571198