摘要
Ilmenite is natural mineral ore made up with titanium and iron mineral; including small portion of magnesium and manganese. To the best of our knowledge, photo-degradation of Reactive Black 5 dye（RB5） using ilmenite under solar irradiation is still lacking. In the present study, the physicochemical properties of ilmenite were characterized by using X-ray diffraction（XRD）, Scanning electron microscope（SEM）, BET and Raman Spectroscopy. Based on our results obtained, 73% solar-driven photo-degradation of RB 5 was successfully obtained when the catalyst loading increased up to 2.0 g/L for 20 min. In general,the photo-degradation of RB 5 by ilmenite followed first-order kinetics. The p H had a significant effect,with the most rapid degradation occurring at p H less than 7.
Ilmenite is natural mineral ore made up with titanium and iron mineral; including small portion of magnesium and manganese. To the best of our knowledge, photo-degradation of Reactive Black 5 dye（RB5） using ilmenite under solar irradiation is still lacking. In the present study, the physicochemical properties of ilmenite were characterized by using X-ray diffraction（XRD）, Scanning electron microscope（SEM）, BET and Raman Spectroscopy. Based on our results obtained, 73% solar-driven photo-degradation of RB 5 was successfully obtained when the catalyst loading increased up to 2.0 g/L for 20 min. In general,the photo-degradation of RB 5 by ilmenite followed first-order kinetics. The p H had a significant effect,with the most rapid degradation occurring at p H less than 7.
基金
supported by Fundamental Research Grant Scheme(No.FRGS:FP008-2015A)
Postgraduate Research Grant(No.PPP:PG050-2015A)
Research Officer Grant Scheme(No.BR006-2015)
Science Fund(No.MOSTI:03-01-03-SF1032)
Trans Disciplinary Research Grant Scheme(No.TR002-2015A)
Prototype Research Grant Scheme(No.PR002-2016)