摘要
为提高氢氧化铝(ATH)的热稳定性能,推广其在电子封装、线路板等电子电工行业中的应用,采用无机纳米颗粒作为改性剂,通过分子间的强作用力,对ATH表面包覆处理,制备出耐热性ATH阻燃剂,通过差热扫描量热分析仪(DSC)对产品进行热稳定性分析。结果表明,经无机纳米颗料表面改性处理后,样品1%分解温度大于260℃,全脱水量大于29%,纯化后产品电导率(EC)低于20μs/cm,能满足于电子级ATH阻燃剂使用要求。
In order to improve the thermal stability of aluminum hydroxide(ATH),and to broaden its application in electronic packaging,electronic circuit boards and other electrical industries.The high dehydration temperature ATH was preparation with surface modification by the inorganic nanopartical.The thermal stability was characterized by differential scanning calorimeter(DSC).The results showed that the decomposition temperature of 1% samples was higher than 260℃ and the amount of all dehydration was more than 29%.Electronic conductivity(EC)was less than 20uS/cm,and can be satisfied to the use of electronic-grade ATH flame retardant requirements.
出处
《化工新型材料》
CAS
CSCD
北大核心
2017年第8期173-175,共3页
New Chemical Materials
关键词
氢氧化铝阻燃剂
表面处理
无机纳米颗粒
热稳定性
ATH flame retardant
surface modification
inorganic nanopatical
thermal stability