摘要
采用无甲醛树脂Arkofix NZF对竹纤维家纺面料进行防缩防皱整理,探讨了树脂用量、催化剂用量、pH值、焙烘温度及时间对竹纤维家纺面料性能的影响。在单因素试验的基础上,通过正交试验方法优化了整理工艺。结果表明,最佳整理工艺为树脂Arkofix NZF 165g/L,六水合氯化镁12g/L,整理液pH值4.0,焙烘温度140℃,焙烘时间2min。整理后织物的折皱回复角提高了97°,缩水率降至3%以下。
Anti-shrink and anti-wrinkle finishing of bamboo home textile fabric was carried out with formaldehyde-free resin Arko- fix NZF. The influences of dosage of resin finishing agent and catalyst, pH value, curing time and temperature on the performances of bamboo home textile fabric were discussed. On the basis of single factor test, the finishing process was optimized by orthogonal test method. The results showed that the optimum finishing process was Arkofix NZF resin 165 g/L, MgCl2 · 6H2O 12 g/L, pH value 4.0, curing at 140 ℃for 2 min. The crease recovery angle of finished fabric increased by 97° and the washing shrinkage decreased to below 3%.
出处
《纺织科技进展》
CAS
2017年第9期26-29,共4页
Progress in Textile Science & Technology
基金
南通市前沿与关键技术创新-工业创新科技项目(GY22015026)
关键词
竹纤维
无甲醛树脂
防缩防皱整理
bamboo fiber
formaldehyde-free resin
anti-shrink and anti-wrinkle finishing