Porous LiMn2O4 hollow microspheres were facilely prepared by incorporation of Li and Mn elements into a spherical polymeric precursor through copolymerization of lithium and manganese acetates with resorcinol and hexamethylenetetramine and then burning off the organic matrix at appropriate temperatures in air. The LiMn2O4 inherited the spherical morphology of the polymeric precursor but showed hollow porous structure assembled by nanocrystals of about 50–100 nm in size. When tested as cathode of Li-ion batteries, the LiMn2O4 hollow spheres exhibited excellent rate capability and cycle stability.A discharge capacity of above 90 mAh g-1was maintained at 10 C（1C = 120 mAg-1）, and the cells can still deliver a discharge capacity over 100 mAhg-1after another 115 cycles at 0.5 C. With such excellent electrochemical properties, the prepared LiMn2O4 hollow microspheres could be promising cathode of Li-ion batteries for long term and high power applications.
Porous LiMn2O4 hollow microspheres were facilely prepared by incorporation of Li and Mn elements into a spherical polymeric precursor through copolymerization of lithium and manganese acetates with resorcinol and hexamethylenetetramine and then burning off the organic matrix at appropriate temperatures in air. The LiMn2O4 inherited the spherical morphology of the polymeric precursor but showed hollow porous structure assembled by nanocrystals of about 50–100 nm in size. When tested as cathode of Li-ion batteries, the LiMn2O4 hollow spheres exhibited excellent rate capability and cycle stability.A discharge capacity of above 90 mAh g-1was maintained at 10 C（1C = 120 mAg-1）, and the cells can still deliver a discharge capacity over 100 mAhg-1after another 115 cycles at 0.5 C. With such excellent electrochemical properties, the prepared LiMn2O4 hollow microspheres could be promising cathode of Li-ion batteries for long term and high power applications.
基金
supported by Natural Science Foundation of Fujian Province (2016J01746 and 2016H0038)
"Minjiang Scholarship" program (60815002)
the start-up fund of XMUT (E2015027 and E2016005)