A facile method for the preparation of sodium alginate（SA）/carboxyl-functionalized graphene（G-COOH）composite hydrogel was developed. Based on the coordination ability of lanthanide ions to the carboxyl groups, a series of hydrogel derived from different ratios of SA and G-COOH was fabricated by neodymium（Nd3＋） ions coordination. A relatively uniform layered structure was recorded by SEM at the interior of SA/G-COOH hydrogel. Several parameters such as water content, swelling ratio（SR）, tensile test and solvent resistance were also investigated. The SA/G-COOH composite hydrogel showed excellent mechanical strength, and the tensile strength of SA/G-COOH composite hydrogel reaches 53.72 MPa at high water content. Due to the coordination ability of Nd3＋ ions, the hydrogel also exhibited an excellent solvent resistance and stability.
A facile method for the preparation of sodium alginate（SA）/carboxyl-functionalized graphene（G-COOH）composite hydrogel was developed. Based on the coordination ability of lanthanide ions to the carboxyl groups, a series of hydrogel derived from different ratios of SA and G-COOH was fabricated by neodymium（Nd3＋） ions coordination. A relatively uniform layered structure was recorded by SEM at the interior of SA/G-COOH hydrogel. Several parameters such as water content, swelling ratio（SR）, tensile test and solvent resistance were also investigated. The SA/G-COOH composite hydrogel showed excellent mechanical strength, and the tensile strength of SA/G-COOH composite hydrogel reaches 53.72 MPa at high water content. Due to the coordination ability of Nd3＋ ions, the hydrogel also exhibited an excellent solvent resistance and stability.
基金
supported by the National Natural Science Foundation of China under Grant Nos.21274020 and 21304019