In this study, Cf/Al composites and TiAl alloys were joined by a new method named laser-ignited selfpropagating synthesis（SHS）. Mixed powders of 63.0Ni-31.9Al-5.1Ti（wt%） were used as joining interlayer.Perfect joint was got. The microstructure evolution and formation mechanism of the SHS joint were investigated by scanning electron microscopy（SEM）, energy-dispersive spectroscopy（EDS） and X-ray diffraction（XRD）. Results show that localized melting occurs on both sides. One γ-Ni（0.35）Al（0.30）Ti（0.35） and two Ni-Al reaction layers form,respectively, in the TiAl/interlayer and Cf/Al/interlayer interfaces. The combustion of Ni-Al-Ti interlayer begins with the sharp reaction of Ni and Al. The interlayer product is a eutectic organization of NiAl and Al-rich γ.
In this study, Cf/Al composites and TiAl alloys were joined by a new method named laser-ignited selfpropagating synthesis（SHS）. Mixed powders of 63.0Ni-31.9Al-5.1Ti（wt%） were used as joining interlayer.Perfect joint was got. The microstructure evolution and formation mechanism of the SHS joint were investigated by scanning electron microscopy（SEM）, energy-dispersive spectroscopy（EDS） and X-ray diffraction（XRD）. Results show that localized melting occurs on both sides. One γ-Ni（0.35）Al（0.30）Ti（0.35） and two Ni-Al reaction layers form,respectively, in the TiAl/interlayer and Cf/Al/interlayer interfaces. The combustion of Ni-Al-Ti interlayer begins with the sharp reaction of Ni and Al. The interlayer product is a eutectic organization of NiAl and Al-rich γ.
基金
financially supported by the National Natural Science Foundation of China(No.51075101)