摘要
Cavitation erosion （CE） is the predominant cause for the failure of overflow components in fluid machinery. Advanced coatings have provided an effective solution to cavitation erosion due to the rapid development of surface engineering techniques. However, the influence of coating structures on CE resistance has not been sys- tematically studied. To better understand their relationship, micro-nano and conventional WC-10Co4Cr cermet coat- ings are deposited by high velocity oxygen fuel spray- ing（HVOF）, and their microstructures are analyzed by OM, SEM and XRD. Meanwhile, characterizations of mechan- ical and electrochemical properties of the coatings are carried out, as well as the coatings＇ resistance to CE in 3.5 wt % NaC1 solution, and the cavitation mechanisms are explored. Results show that micro-nano WC-10Co4Cr coating possesses dense microstructure, excellent mechanical and electrochemical properties, with very low porosity of 0.26 4-0.07% and extraordinary fracture toughness of 5.58 4-0.51 MPa.m1/2. Moreover, the CE resistance of micro-nano coating is enhanced above 50% than conventional coating at the steady CE period in 3.5 wt % NaC1 solution. The superior CE resistance of micro- nano WC-10Co4Cr coating may originate from the unique micro-nano structure and properties, which can effectively obstruct the formation and propagation of CE crack. Thus,a new method is proposed to enhance the CE resistance of WC-10Co4Cr coating by manipulating the microstructure.
Cavitation erosion （CE） is the predominant cause for the failure of overflow components in fluid machinery. Advanced coatings have provided an effective solution to cavitation erosion due to the rapid development of surface engineering techniques. However, the influence of coating structures on CE resistance has not been sys- tematically studied. To better understand their relationship, micro-nano and conventional WC-10Co4Cr cermet coat- ings are deposited by high velocity oxygen fuel spray- ing（HVOF）, and their microstructures are analyzed by OM, SEM and XRD. Meanwhile, characterizations of mechan- ical and electrochemical properties of the coatings are carried out, as well as the coatings＇ resistance to CE in 3.5 wt % NaC1 solution, and the cavitation mechanisms are explored. Results show that micro-nano WC-10Co4Cr coating possesses dense microstructure, excellent mechanical and electrochemical properties, with very low porosity of 0.26 4-0.07% and extraordinary fracture toughness of 5.58 4-0.51 MPa.m1/2. Moreover, the CE resistance of micro-nano coating is enhanced above 50% than conventional coating at the steady CE period in 3.5 wt % NaC1 solution. The superior CE resistance of micro- nano WC-10Co4Cr coating may originate from the unique micro-nano structure and properties, which can effectively obstruct the formation and propagation of CE crack. Thus,a new method is proposed to enhance the CE resistance of WC-10Co4Cr coating by manipulating the microstructure.
基金
Supported by National Natural Science Foundation of China (Grand No. 51422507)