摘要
Three-dimensional porous nitrogen-doped graphene aerogels （NGAs） were synthesized by using graphene oxide （GO） and chitosan （CS） via a self-assembly process by one-pot hydrothermal method. The morphology and struc- ture of the as-prepared materials were characterized by means of scanning electron microscopy, transmission elec- tron microscopy, X-ray diffraction, XPS spectroscopy, Raman spectroscopy, nitrogen adsorption/desorption meas- urement and Fourier transform infrared spectroscopy. The electrochemical performance of NGAs was studied by cyclic voltammetry, galvanostatic charge/discharge and impedance spectroscopy measurements. The microstructure, surface area and capacitance of NGAs could be facilely controlled by adding different amounts of chitosan. The prepared NGA-4 showed a specific capacitance of 148.0 F/g at the discharge current density of 0.5 A/g and also re- tained 95.3% of the initial capacitance after 5000 cycles at the scan rate of 10 mV/s. It provided a possible way to obtain graphene based materials with high surface area and capacitance.
Three-dimensional porous nitrogen-doped graphene aerogels （NGAs） were synthesized by using graphene oxide （GO） and chitosan （CS） via a self-assembly process by one-pot hydrothermal method. The morphology and struc- ture of the as-prepared materials were characterized by means of scanning electron microscopy, transmission elec- tron microscopy, X-ray diffraction, XPS spectroscopy, Raman spectroscopy, nitrogen adsorption/desorption meas- urement and Fourier transform infrared spectroscopy. The electrochemical performance of NGAs was studied by cyclic voltammetry, galvanostatic charge/discharge and impedance spectroscopy measurements. The microstructure, surface area and capacitance of NGAs could be facilely controlled by adding different amounts of chitosan. The prepared NGA-4 showed a specific capacitance of 148.0 F/g at the discharge current density of 0.5 A/g and also re- tained 95.3% of the initial capacitance after 5000 cycles at the scan rate of 10 mV/s. It provided a possible way to obtain graphene based materials with high surface area and capacitance.
基金
We are grateful to Research Center of Laser Fusion, China Academy of Engineering Physics. This work was financially supported by the National Natural Science Foundation of China （No. 51502274）, the Research Fund for the Doctoral Program of Southwest University of Science and Technology （Nos. 13zx7124, 15zx7137, 16zx7142） and the Research Fund for Joint Laboratory for Extreme Conditions Matter Properties （Nos. 13zxjk04, 14tdjk03）.