The effect of dissolved niobium on the eutectoid transformation behavior in near-eutectoid high-carbon steels has been studied.Dissolved niobium is important in the eutectoid transformation behavior.It increases the eutectoid carbon content significantly（by^0.0477% per 0.00001% dissolved niobium）,increases the hardenability of steel markedly,yields finer,more uniform,polygonal proeutectoid ferrite,induces a transition in morphology of eutectoid cementite from lamellar to somewhat spheroidal,and increases the misorientation angle of pearlite colonies from being focused near 0°to near 60°.
The effect of dissolved niobium on the eutectoid transformation behavior in near-eutectoid high-carbon steels has been studied.Dissolved niobium is important in the eutectoid transformation behavior.It increases the eutectoid carbon content significantly（by^0.0477% per 0.00001% dissolved niobium）,increases the hardenability of steel markedly,yields finer,more uniform,polygonal proeutectoid ferrite,induces a transition in morphology of eutectoid cementite from lamellar to somewhat spheroidal,and increases the misorientation angle of pearlite colonies from being focused near 0°to near 60°.