摘要
A CaF2-CeF3 disordered crystal containing 1.06% of Er^3＋ ions was grown by the temperature gradient technique.Optical absorption and emission spectra recorded at room temperature and at 10 K, luminescence decay curve recorded at room temperature, and extended x-ray-absorption fine structure spectra were analyzed with an intention to assess the laser potential related to the ^4I13/2→^4I15/2 transition of Er^3＋. In addition, the thermal diffusivity of the crystal was measured at room temperature. The analysis of room-temperature spectra revealed that the ^4I13/2 emission is long-lived with a radiative lifetime value of 5.5 ms, peak emission cross section of 0.73 × 10^-20 cm^2, and large spectral width pointing at the tunability of the emission wavelength in the region stretching from approximately 1480 nm to 1630 nm. The energies of the crystal field components for the ground and excited multiplets determined from low-temperature absorption and emission spectra made it possible to predict successfully the spectral position and shape of the room-temperature ^4I13/2→^4I15/2 emission band. Based on the correlation of the optical spectra and dynamics of the luminescence decay, it was concluded that in contrast to Yb^3＋ ions in heavily doped CaF2 erbium ions in the CaF2-CeF3 crystal reside in numerous sites with dissimilar relaxation rates.
A CaF2-CeF3 disordered crystal containing 1.06% of Er^3＋ ions was grown by the temperature gradient technique.Optical absorption and emission spectra recorded at room temperature and at 10 K, luminescence decay curve recorded at room temperature, and extended x-ray-absorption fine structure spectra were analyzed with an intention to assess the laser potential related to the ^4I13/2→^4I15/2 transition of Er^3＋. In addition, the thermal diffusivity of the crystal was measured at room temperature. The analysis of room-temperature spectra revealed that the ^4I13/2 emission is long-lived with a radiative lifetime value of 5.5 ms, peak emission cross section of 0.73 × 10^-20 cm^2, and large spectral width pointing at the tunability of the emission wavelength in the region stretching from approximately 1480 nm to 1630 nm. The energies of the crystal field components for the ground and excited multiplets determined from low-temperature absorption and emission spectra made it possible to predict successfully the spectral position and shape of the room-temperature ^4I13/2→^4I15/2 emission band. Based on the correlation of the optical spectra and dynamics of the luminescence decay, it was concluded that in contrast to Yb^3＋ ions in heavily doped CaF2 erbium ions in the CaF2-CeF3 crystal reside in numerous sites with dissimilar relaxation rates.
基金
Project supported by Shanghai Engineering Research Center for Sapphire Crystals,China(Grant No.14DZ2252500)
the Fund of Key Laboratory of Optoelectronic Materials Chemistry and Physics Chinese Academy of Sciences(Grant No.2008DP17301)
the Fundamental Research Funds for the Central Universities of China
the National Natural Science Foundation of China and China Academy of Engineering Physics Joint Fund(Grant No.U1530152)
the National Natural Science Foundation of China(Grant Nos.61475177 and 61621001)
the Natural Science Foundation of Shanghai Municiple,China(Grant No.13ZR1446100)
the MOE Key Laboratory of Advanced Micro-Structured Materials of China