摘要
利用Thermecmastor-Z热模拟试验机对试验用耐磨钢的金属塑性变形抗力进行研究,获得了该钢种在1200℃,应变速率为1、10 s-1的应力-应变曲线。应用ANSYS/LS-DYNA有限元软件模拟了1200℃条件下耐磨钢/碳钢复合板的单道次轧制过程。结果表明:在单道次轧制过程中,获得理想的复合效果的垂直压应力要达到200 MPa以上,等效应变要达到0.85以上。
The metal plastic deformation resistance of the wear resistant steel was studied by Thermecmastor-Z thermal simulator and then the stress-strain curves of the steel at 1200 ℃ and strain rate of 1s1 and 10 s-1 were obtained. The single channel rolling process of wear resistant steel and carbon steel composite plate at 1200℃ was simulated by ANSYS/LS-DYNA finite element software. The results show that in the process of rolling in single channel, the ideal compound effect can be obtained by the vertical compressive stress reaching above 200 MPa and the equivalent strain reaching above 0.85.
作者
兰昆
程晓茹
邱俊
雷冬
彭玉
黄大军
LAN Kun CHENG Xiaoru QIU Jun LEI Dong PENG Yu HUANG Dajun(Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan 430081, China Wuhan Iron and Steel Co., Ltd., Wuhan 430083, China)
出处
《热加工工艺》
CSCD
北大核心
2017年第20期121-124,共4页
Hot Working Technology
关键词
变形抗力
有限元
耐磨钢复合板
最大垂直压应力
等效应变
deformation resistance
FEM
wear-resistant steel composite plate
maximum vertical compressive stress
equivalent strain