摘要
采用Pd2+活化结合化学镀镍工艺制备金属化的植物纤维无纺布,借助X射线衍射、扫描电镜、四探针等分析测试手段,研究化学镀时间对植物纤维无纺布表面镀镍层结构特性的影响规律。结果表明延长化学镀时间,植物纤维无纺布表面化学镀镍层结晶性能变好。当化学镀时间为10min时,植物纤维无纺布的质量为0.038g/cm2,镀层表面电阻率为0.2Ω·cm。
The metalization of plant fiber non-woven paper were prepared by Pd2＋activating-electroless nickel plating.The effects of plated time on Ni coating on plant fiber non-woven paper were investigated using X-ray diffraction electron microscopy,scanning electron microscopy and four probe method.Results showed that the crystallization of plated coating increased with increase of plated time.The weigh of non-woven paper after electroless nickel plating was0.038 g/cm2,the surface electrical resistivity was 0.2Ω·cm,when the plated time was 10 min.
作者
黄俊俊
王辉
陈珍明
孙志平
高敏
李梦雨
刘琦
程薇
Huang Junjun Wang Hui Chen Zhenming Sun Zhiping Gao Min Li Mengyu Liu Qi Cheng Wei(Hefei Lucky ＆ Technology Industry Co., Ltd., Hefei 230041 Department of Chemical and Materials Engineering, H efei College, Hefei 230601 College of Chemistry and Bioengineering, Hezhou University, Hezhou 542899 Research Institute of Surface Engineering,Taiyuan University of Technology,Taiyuan 030024)
出处
《化工新型材料》
CAS
CSCD
北大核心
2017年第10期196-198,共3页
New Chemical Materials
基金
中国科学院能量转换材料重点实验室开放课题基金(KF2016001)
安徽省教育厅一般项目(KJ2015B1105905
KJ2015B1105906)
关键词
非织造布
化学镀
镍镀层
纤维
non-woven paper, electroless plating, nickel-plated coating, fiber