真空包压敏耐高温(200℃)密封胶条研制

Study of pressure-sensitive high-temperature-resistant(200℃)sealant tape for vacuum bagging
下载PDF
导出
摘要 使用丁基橡胶、酚醛硫化剂、氧化钙、聚异丁烯和滑石粉为原料,制备真空包压敏耐高温(200℃)密封胶条,研究了各原料对密封胶条性能的影响。结果表明,制备的密封胶条有较好的力学性能、密封性能和耐高温性能。室温拉剪强度>0.17 MPa,拉断伸长率>700%,200℃、6 h加热后室温拉剪强度为0.19~0.35 MPa,高温使用后室温剥离不留残余。200℃真空包固化12 h内不泄漏,抽真空压强接近0.1 MPa。 The pressure-sensitive high-temperature-resistant(200 ℃) sealant tape for vacuum bagging was prepared successfully by using the butyl rubber, phenolic vulcanizing agent, CaO, polyisobutylene and talc as the raw materials, and the effect of raw materials on the properties of sealant tape was studied. The results showed that the sealant tape had good mechanical and sealing properties. The lap tensile shear strength at room temperature was over 0.17 MPa, the elongation at break at room temperature was over 700%, the tensile tear strength at room temperature was between 0.19 - 0.35 MPa after heating at 200 ℃ for 6 h, and when room temperature peeling there was no residue after high temperature use. The vacuum bagging had no leak at 200 ℃ for 12 h when the exhausted pressure remained about 0.1 MPa.
出处 《粘接》 CAS 2017年第12期25-28,共4页 Adhesion
关键词 密封胶条 真空包 耐高温 压敏性 sealant tape vacuum bagging high temperature resistance pressure sensitivity
  • 相关文献

参考文献2

二级参考文献30

  • 1盘毅,胡芸,宋威.二酚基甲烷的合成与表征[J].国防科技大学学报,2005,27(2):15-19. 被引量:13
  • 2屈乃琴.先进复合材料的研究现状与应用[J].纤维复合材料,1995,12(1):45-54. 被引量:14
  • 3李小兵,孙占红,曹正华.真空辅助成型技术及其配套基体树脂研究进展[J].热固性树脂,2006,21(5):39-43. 被引量:23
  • 4阮桂海.丁基橡胶应用工艺[M].-,..
  • 5北京橡胶工业研究设计院 丁基橡胶专题组.丁基橡胶的基本应用性能[J].橡胶工业,1998,(2):1-5.
  • 6Sun X D, Li S J, Lee L J. Mold filling analysis in vacuum-assisted resin transfer molding, Part I: SCRIMP Based on High-Permeable Medium [ J ]. Polymer Composites, 1998, 19 ( 6 ) : 807-817.
  • 7Sun X D, Li S J, Lee L J. Mold filling analysis in vacuum-assisted resin transfer molding,Part Ⅱ :SCRIMP Based on High-Permeable Medium[ J]. Polymer Composites, 1998, 19(6) : 818-829.
  • 8Mathur R, Heider D, Hoffmann C, et al. Flow front measurements and model validation in the vacuum assisted resin transfer molding process[J]. Polym Compos, 2001,22(4) : 477-490.
  • 9Rigas E J,Wanlsh SM, William A S. Development of a novel processing technique for vacuum assisted resin transfer molding (VARTM)[A]. In: SAMPLE[C]. 2001.
  • 10Hammami A , Gebart B R. Experimental investigation of the vacuum infusion process [ A ]. In : Proceedings of ECCM-8 [ C ]. 1998.

共引文献44

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部