多孔质生态混凝土作为一种新型的工程材料,已受到国内外学者的广泛关注与研究。该项目采用特有的制备与成型工艺制备多孔质生态混凝土,分别研究了水灰比和粗骨料对多孔质生态混凝土的孔隙率及抗压强度的影响。结果表明,水灰比及粗骨料的级配对多孔质生态混凝土的孔隙率及抗压强度影响较大。
As a new type of engineering material, porous eco-concrete has been increasingly stressed and studied by scholars at home and abroad. This project adopts special preparation and molding techniques to produce porous eco-concrete, and studies the impact of water-cement ratio and coarse aggregate on the porosity and compressive strength of porous eco-concrete. The results show that water-cement ratio and coarse aggregate gradation have great influence on porosity and compressive strength of porous eco-concrete.