摘要
目的通过观察渗透树脂与多乐氟处理脱矿釉质后其牙齿表面显微硬度和粗糙度的变化,对两种材料在釉质抗酸性和再矿化能力方面的性能进行评估。方法选择正畸拔除的健康前磨牙48颗,建立釉质表面脱矿模型,按照不同材料的处理条件随机分为4组,A(不做任何处理),B(渗透树脂),C(多乐氟);D(渗透树脂+多乐氟),分别经脱矿液组(1d,3d)和再矿化液组(7d)浸泡处理后,测定牙齿表面的显微硬度和粗糙度。结果不同材料处理脱矿模型后即刻,B、D组的显微硬度、粗糙度均明显增加(P<0.001),B、D组之间无统计学差异(P>0.05);而C组显微硬度、粗糙度均明显减低(P<0.001)。继续脱矿(1d,3d)后,各组的显微硬度均下降,而粗糙度却明显增加;再矿化7d后,A、C组显微硬度和粗糙度均显著增加(P<0.001),B、D组增加不明显(P>0.05)。结论渗透树脂具有良好的改善牙齿表面硬度的作用,但在抗酸性和促进牙齿再矿化方面无明显优势。而氟化物则在抗酸性和促进再矿化方面有突出表现。当两者联合应用时,可以起到较好协同作用,明显增强牙齿的硬度、抗酸性和再矿化性能。
Objective To evaluate effect of infiltration resin and fluoride treatment on the repair, acid resistance and remineralization of enamel based on the observation of the hardness and surface roughness of enamel carious lesions. Methods Used forty-eight human premolars extracted for orthodontic purpose to obtain artificial subsurface lesions. Then artificial enamel caries lesions were divided into four groups. Group A, no treatment; Group B, resin infiltration (Icon); Group C, Duraphat; Group D, resin infiltration + Duraphat. The micro-Vickers hardness test and Talysurf were used to investigate the change in hardness and surface roughness of enamel. Then, each group was randomly divided into two subgroups, one was soaked in demineralization buffer (2.2 mmol/L Ca(NO3):, 2.2 mmol/L KH2PO4, 50 mmol/L ethylic acid, 1.0 mmol/L NAN,, 0.1 mmol/L NaF, pH=4.5) (1 d, 3 d) and the other in mineralization buffer (0.4 g/L NaCI, 0.4 g/L KCl, 0.795 g/L CaCl2, 1 g/L urea, 0.005 g/L Na2S·2H2O, 0.78 g/L NaH2PO4·H2O, pH=6.8) (7 d), and measure the Vickers hardness number (VHN) and roughness of enamelsurface (Sa) again. Result After 3-d demineralization, the VHN and Sa of groups B and D were significantly higher than group A (P〈0.001), while there was no difference between groups B and D (P〉0.05). The VHN and Sa of group C were obviously smaller than other groups (P〈0.001). Compared with demineralization, the VHN of 1 day and 3 days post treatment were markedly decreased while the Sa was significantly increased. After 7 days mineralization, the VHN and Sa were increased especially in groups A and C (P〈0.001), while there were no difference between groups B and D in Sa (P〉0.05). Conclusion Resin infiltration increased the VHN of carious and improved the surface structure, while there was no obvious advantage in acid resistance and remineralization, However, fluoride can improve this problem. After the treatment with fluoride and resin infiltration, significant enhancement of hardness, acid resistance and remineralization of enamel carious lesions was observed in our study.
出处
《口腔材料器械杂志》
2017年第4期191-197,共7页
Chinese Journal of Dental Materials and Devices
关键词
渗透树脂
多乐氟
脱矿釉质
表面粗糙度
显微硬度
Resin infiltration Duraphat Demineralization of enamel Surface roughness Microhardness