摘要
The Luders deformation behavior in a medium Mn transformation induced plasticity （TRIP） steel is investigated at different temperatures ranging from 25 to 300 ℃. It demonstrates that the Ltiders band appears at all testing temperatures but with varied Luders strains which do not change monoton ically with temperature. The martensitic transformation is simultaneously observed within the Ltiders band in varying degrees depending on the testing temperature. It is well verified that the martensitic transformation is not responsible for the formation of Luders band, and a reasonable explanation is given for the non-monotonic variation of Luders strain with increasing temperature.
The Luders deformation behavior in a medium Mn transformation induced plasticity （TRIP） steel is investigated at different temperatures ranging from 25 to 300 ℃. It demonstrates that the Ltiders band appears at all testing temperatures but with varied Luders strains which do not change monoton ically with temperature. The martensitic transformation is simultaneously observed within the Ltiders band in varying degrees depending on the testing temperature. It is well verified that the martensitic transformation is not responsible for the formation of Luders band, and a reasonable explanation is given for the non-monotonic variation of Luders strain with increasing temperature.
基金
support from the Steel Joint Funds of the National Natural Science Foundation of China(Grant No.U1560204)
Research Grants Council of Hong Kong(Grant Nos.HKU719712E,HKU712713E)
Small Project Funding of HKU(Grant No.201409176053)