A novel microorganism embedding material was prepared to enhance the biological nitrogen removal through simultaneous nitrification and denitrification. Polyvinyl alcohol （PVA）, sodium alginate （SA） and cyclodextrin （CD） were used to compose gel bead with embedded activated sludge. The effects of temperature, CD addition and concentrations of PYA and SA on nitrogen removal were evaluated. Results show that the gel bead with CD addition at 30℃contributed to the highest nitrogen removal efficiency and nitrogen removal rate of 85.4% and 2.08 mg·（L·h）^-1, respectively. Meanwhile, negligible NO3^- and NO2^- were observed, proving the occurrence of simultaneous nitrification and denitrification. The High-Throughput Sequencing confirms that the microbial community mainly contained Comamonadaceae in the proportion of 61.3%. Overall, CD increased gel bead＇s porosity and resulted in the high specific endogenous respiration rate and high nitrogen removal efficiency, which is a favorable additional agent to the traditional embedding material.
A novel microorganism embedding material was prepared to enhance the biological nitrogen removal through simultaneous nitrification and denitrification. Polyvinyl alcohol （PVA）, sodium alginate （SA） and cyclodextrin （CD） were used to compose gel bead with embedded activated sludge. The effects of temperature, CD addition and concentrations of PYA and SA on nitrogen removal were evaluated. Results show that the gel bead with CD addition at 30℃contributed to the highest nitrogen removal efficiency and nitrogen removal rate of 85.4% and 2.08 mg·（L·h）^-1, respectively. Meanwhile, negligible NO3^- and NO2^- were observed, proving the occurrence of simultaneous nitrification and denitrification. The High-Throughput Sequencing confirms that the microbial community mainly contained Comamonadaceae in the proportion of 61.3%. Overall, CD increased gel bead＇s porosity and resulted in the high specific endogenous respiration rate and high nitrogen removal efficiency, which is a favorable additional agent to the traditional embedding material.
基金
Acknowledgements This research was financially supported by Natural Science Foundation of Tianjin （Nos. 15JCYBJC53700 and 14JCYBJC- 43700）, National Undergraduate Training Programs for Innovation and Entrepreneurship （No. 201610057005）, Scientific Research Foundation for the Returned Overseas Chinese Scholars of State Education Ministry.