Effect of SiO2 Micropowder Addition on Properties of Alumina-magnesia Based Wet Gunning Mix for Working Layer

Effect of SiO_2 Micropowder Addition on Properties of Alumina-magnesia Based Wet Gunning Mix for Working Layer
下载PDF
导出
摘要 The magnesia - alumina based wet gunning mix was prepared using tabular corundum aggregates,fused mag- nesia aggregates, tabular corundum micropowder, silica mieropowder and pure calcium ahuninate cement as the main starting materials. Effects of silica micropowder ad- ditions (0, 0. 2% , 0. 5% , 1.0% , 1.5% , 2. 0% , and 2.5%, by mass, the same hewinafier) on properties oJ the gunning mix were researched. The results show that when ttze silica micropowder addition is i. 0% -2. 0% , the gunning mix has good .flou,ability and pumpability. Adding 2.5% silica micropowder, the nepheline forms at 1 600 ℃, which will reduce the high. temperature proper- ties of ntagnesia -ahtmina wet gunning mix. The intro- duction qf silica micropowder has obvious effects on cold mechanical properties of the gunning mix. For the speci- tnens dried at 110 ℃ , the strength increases slightly with the silica micropowder addition increasing. For the specimens heat-treated at 1 600 ℃ for 3 h, the strength in- creases nutrkedlv with the silica micropowder addition in- creasing. When keeping the water addition and particle size di, stribution constant, the residual linear expansion rate qf the specimen with 1.5% of silica micropowder is the lowest, ltot modulus tf rupture at 1 450 ℃ .for 0. 5 h oJ the specimens decreases gradually with the increase of silica fame addition. A small amount of silica micropow- der is beneficial for the slag penetration resistance. The magnesia - alumina based wet gunning mix was prepared using tabular corundum aggregates,fused mag- nesia aggregates, tabular corundum micropowder, silica mieropowder and pure calcium ahuninate cement as the main starting materials. Effects of silica micropowder ad- ditions (0, 0. 2% , 0. 5% , 1.0% , 1.5% , 2. 0% , and 2.5%, by mass, the same hewinafier) on properties oJ the gunning mix were researched. The results show that when ttze silica micropowder addition is i. 0% -2. 0% , the gunning mix has good .flou,ability and pumpability. Adding 2.5% silica micropowder, the nepheline forms at 1 600 ℃, which will reduce the high. temperature proper- ties of ntagnesia -ahtmina wet gunning mix. The intro- duction qf silica micropowder has obvious effects on cold mechanical properties of the gunning mix. For the speci- tnens dried at 110 ℃ , the strength increases slightly with the silica micropowder addition increasing. For the specimens heat-treated at 1 600 ℃ for 3 h, the strength in- creases nutrkedlv with the silica micropowder addition in- creasing. When keeping the water addition and particle size di, stribution constant, the residual linear expansion rate qf the specimen with 1.5% of silica micropowder is the lowest, ltot modulus tf rupture at 1 450 ℃ .for 0. 5 h oJ the specimens decreases gradually with the increase of silica fame addition. A small amount of silica micropow- der is beneficial for the slag penetration resistance.
机构地区 Zhejiang Zili Co.
出处 《China's Refractories》 CAS 2017年第4期12-16,共5页 中国耐火材料(英文版)
关键词 silica micropowder alumina- magnesia based wet gunning mix slag resistance silica micropowder alumina- magnesia based wet gunning mix slag resistance
  • 相关文献

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部