摘要
Five lightweight castables containing different TiO2 additions were prepared by using porous corundum - spinel （ MgAl2O4 ） ceramics as aggregate. Corrosion of the lightweight cstables by ladle slag was conducted using a static crucible test. The effect of the TiO2 addition on the slag resistances of the lightweight corundum -spinel castables was investigated through SEM, EDS and Fact- Sage@ software, etc. h was found that TiO2 additi,ve t,vmoted the sintering degree of the castables, deereased the average pore .size, the apparent porosity, and the contact area between the casmbles and slag, and then en- hanced the corrosion resistance. However, TiO2 additive decreased the viscosity of the penetrated .slag simultane- ously, and then deteriorated the penetration resistance.
Five lightweight castables containing different TiO2 additions were prepared by using porous corundum - spinel （ MgAl2O4 ） ceramics as aggregate. Corrosion of the lightweight cstables by ladle slag was conducted using a static crucible test. The effect of the TiO2 addition on the slag resistances of the lightweight corundum -spinel castables was investigated through SEM, EDS and Fact- Sage@ software, etc. h was found that TiO2 additi,ve t,vmoted the sintering degree of the castables, deereased the average pore .size, the apparent porosity, and the contact area between the casmbles and slag, and then en- hanced the corrosion resistance. However, TiO2 additive decreased the viscosity of the penetrated .slag simultane- ously, and then deteriorated the penetration resistance.
基金
The National Natural Science Foundation of China(Grant No.51302201)