通过真空吸附法,以膨胀珍珠岩(EP)为多孔基体材料,正癸酸(CA)为相变材料,将水泥砂浆与正癸酸/膨胀珍珠岩相变材料混合,制备了正癸酸/膨胀珍珠岩复合相变水泥板,研究了温度、复合相变材料含量等对导热系数的影响。结果表明:相同温度条件下,复合相变材料含量越高,复合相变水泥板的导热系数越低;与普通水泥板相比,复合相变材料含量为8%、13%、18%的水泥板导热系数分别降了40.60%、49.59%、53.43%(21℃)和39.16%、47.89%、51.61%(51℃)。
The n-decanoie acid/expanded perlite composite phase change ,cement board was mixed with n-decanoic acid/ expanded perlite phase change material by vacuum adsorption method with expanded perlite(EP) as the porous matrix material and u-decanoic acid (CA) as phase change material. The effect of temperature and content of phase change material on thermal con- ductivity was researched. The results show that the higher the phase change material content is,the'lower the thermal conductivity of the cement board is under the same temperature condition. Compared with the thermal conductivity of ordinary cement board, the thermal conductivity of 8%, 13% and 18% composite phase change cement slabs decreased by 40.60%,49.59%,53.43% (21 %) and 39.16%, 47.89%, 51.61% (51 ℃).
出处
《新型建筑材料》
北大核心
2017年第12期8-11,共4页
New Building Materials
基金
辽宁省自然科学基金项目(2015020214)
关键词
复合相变材料
水泥板
导热系数
热流密度
composite phase change material,cement board,thermal conductivity,heat flux density