A new hybrid organic-inorganic structure of FTO/TiO2/Se/HTL/Au based selenium solar cell has been fabricated through a low-cost spin-coating process in air. In this process, selenium is completely dissolved in hydrazine, to fk）rm a homogeneous precursor solution. After spin-coating the precursor solution on the TiO2 substrates, following by sintering at 200 ℃ for 5rain, a uniform selenium film with crystalline grains is formed. The selenium based solar cell exhibits an efficiency of 1.23% under AM1.5 illumination （100 mW.cm-2）, short-circuit current density of 8 mA.cm 2, open-circuit voltage of 0.55 V, and fill factor of 0.37. Moreover, the device shows a stable ability with almost the same performance alter 60 days.
A new hybrid organic-inorganic structure of FTO/TiO2/Se/HTL/Au based selenium solar cell has been fabricated through a low-cost spin-coating process in air. In this process, selenium is completely dissolved in hydrazine, to fk）rm a homogeneous precursor solution. After spin-coating the precursor solution on the TiO2 substrates, following by sintering at 200 ℃ for 5rain, a uniform selenium film with crystalline grains is formed. The selenium based solar cell exhibits an efficiency of 1.23% under AM1.5 illumination （100 mW.cm-2）, short-circuit current density of 8 mA.cm 2, open-circuit voltage of 0.55 V, and fill factor of 0.37. Moreover, the device shows a stable ability with almost the same performance alter 60 days.
基金
Project supported by the National Natural Science Foundation of China(Grant Nos.51579057,5177090655,and 51379052)
the State Key Laboratory of Urban Water Resource and Environment,Harbin Institute of Technology,China(Grant No.2016DX07)