摘要
We investigate deformation and spallation of explosive welded bi-steel plates under gas gun shock loading. Free surface histories are measured to obtain the Hugoniot elastic limit and spall strengths at different impact velocities.Pre-and post-shock microstructures are characterized with optical metallography, scanning electron microscopy,and electron backscatter diffraction. In addition, the Vickers hardness test is conducted. Explosive welding can result in a wavy steel/steel interface, an ultrafine grain region centered at the interface, and a neighboring high deformation region, accompanied by a hardness with the highest value at the interface. Additional shock compression induces a further increase in hardness, and shock-induced deformation occurs in the form of twinning and dislocation slip and depends on the local substructure. Spall damage nucleates and propagates along the ultrafine grain region, due to the initial cracks or weak interface bonding. Spall strengths of bimetal plates can be higher than its constituents. Plate impact offers a promising method for improving explosive welding.
We investigate deformation and spallation of explosive welded bi-steel plates under gas gun shock loading. Free surface histories are measured to obtain the Hugoniot elastic limit and spall strengths at different impact velocities.Pre-and post-shock microstructures are characterized with optical metallography, scanning electron microscopy,and electron backscatter diffraction. In addition, the Vickers hardness test is conducted. Explosive welding can result in a wavy steel/steel interface, an ultrafine grain region centered at the interface, and a neighboring high deformation region, accompanied by a hardness with the highest value at the interface. Additional shock compression induces a further increase in hardness, and shock-induced deformation occurs in the form of twinning and dislocation slip and depends on the local substructure. Spall damage nucleates and propagates along the ultrafine grain region, due to the initial cracks or weak interface bonding. Spall strengths of bimetal plates can be higher than its constituents. Plate impact offers a promising method for improving explosive welding.
作者
余颖
李超
马宏昊
祁美兰
罗胜年
Ying Yu1,2,3, Chao Li2,3, Hong-Hao Ma4, Mei-Lan Qi1, Sheng-Nian Luo2,3(1School of Science, Wuhan University of Technology, Wuhan 430070; 2Key Laboratory of Advanced Technologies of Materials （Ministry of Education）, Southwest Jiaotong University Chengdu 610031 ;3 The Peac Institute of Multiscale Sciences, Chengdu 610207 ; 4 CAS Key Laboratory of MateriMs Behavior and Design, Department of Modern Mechanics, University of Science and Technology of China, Hefei 230027)
基金
Supported by the National Basic Research Program of China under Grant No 2014CB845904
the National Natural Science Foundation of China under Grant Nos 11627901,11372113 and 11672110