The potential of bulk-like WTe2 particles for the realization of a passive Q-switch operating at the 1 μm wavelength was investigated. The WTe2 particles were prepared using a simple mechanical exfoliation method together with Scotch tape. By attaching bulk-like WTe2 particles, which remained on the top of the sticky surface of a small segment of the Scotch tape, to the flat side of a side-polished fiber, a saturable absorber（SA） was readily implemented. A strong saturable absorption was then readily obtained through an evanescent field interaction with the WTe2 particles. The modulation depth of the prepared SA was measured as ~2.18% at 1.03 μm. By incorporating the proposed SA into an all-fiberized ytterbium-doped fiber ring cavity, stable Qswitched pulses were readily achieved.
The potential of bulk-like WTe2 particles for the realization of a passive Q-switch operating at the 1 μm wavelength was investigated. The WTe2 particles were prepared using a simple mechanical exfoliation method together with Scotch tape. By attaching bulk-like WTe2 particles, which remained on the top of the sticky surface of a small segment of the Scotch tape, to the flat side of a side-polished fiber, a saturable absorber（SA） was readily implemented. A strong saturable absorption was then readily obtained through an evanescent field interaction with the WTe2 particles. The modulation depth of the prepared SA was measured as ~2.18% at 1.03 μm. By incorporating the proposed SA into an all-fiberized ytterbium-doped fiber ring cavity, stable Qswitched pulses were readily achieved.
作者
高承煥
李珍昊
李周翰
Seunghwan Ko , Jinho Lee , and Ju Han Lee(School of Electrical and Computer Engineering, University of Seoul, Seoul 02504, Republic of Kore)
基金
supported by the National Research Foundation of Korea funded by the Korean Government(MSIT),South Korea(Grant Nos.NRF-2015R1A2A2A11000907 and NRF-2015R1A2A2A04006979)
Ministry of Science and ICT(MSIT),Korea,under the Information Technology Research Center(ITRC)support program(IITP-2017-2015-0-00385),supervised by the Institute for Information and Communications Technology Promotion(IITP)