为了加快聚乳酸（PIA）手术缝合线的降解速度，缩短其降解周期，先用脂肪酶处理缝合线表面，使缝合线表面羟基的数量增多：然后在缝合线表面用壳聚糖进行接枝，研究壳聚糖浓度、壳聚糖处理温度以及壳聚糖处理时间对缝合线的断裂强度、表面结构性能以及亲水性能的影响。得出壳聚糖最优处理工艺为：壳聚糖质量浓度3g／L，处理温度40℃，处理时间4h。
In order to accelerate the degradation rate of PLA suture and shorten the degradation c, suture surface is firstly treated with lipase to increase hydroxyl groups on the surface of PLA, and then chitosan is grafted on the surface of the PLA surgical suture. The influences of chitosan concentration, chitosan treatment temperature and treatment time of chitosan suture on the breaking strength, performance and surface structure the hydrophilicity of chitosan are studied. The optimal process is obtained as treating at 40℃ for 4 h with chitosan 3 g/L.
作者
刘明芳
刘淑强
张晓芳
吴改红
王鹏
郭竑宇
郭红霞
LIU Mingfang, LIU Shuqiang, ZHANG Xiaofang, WU Gaihong, WANG Peng, GUO Hongyu, GUO Hongxia(College of Textile Engineering, Taiyuan University of Technology, Jinzhong 030600, Chin)
出处
《上海纺织科技》
北大核心
2018年第3期25-27,30,共4页
Shanghai Textile Science & Technology
基金
山西省基础研究计划项目(2015021076
2014021020-2)
山西省高等学校科技创新项目(2015125)
山西省高校大学生创新创业训练项目(201673
201758)
山西省研究生教育创新项目(201785)
山西省社科联重点项目(SSKLZDKT2016055)
山西省教育科学“十三五”规划2016年度课题(GH-16014)
关键词
聚乳酸
手术缝合线
壳聚糖
亲水改性
断裂强度
吸湿性
polylactic acid
surgical suture
ehitosan
hydrophilic modification
fracture strength
hydroscopieity