摘要
用大孔超高交联聚苯乙烯树脂(简称HPS树脂)进行硝化反应,得到了硝化修饰的大孔超高交联聚苯乙烯树脂(简称HPS-NO_2树脂)。红外分析、元素分析测定了HPS-NO_2树脂的硝化程度;通过交换量测定确定了HPS-NO_2树脂因氧化反应引入羧基的量。采用氮气吸-脱附法测定了HPS、HPS-NO_2树脂的比表面积和孔结构参数。并考察了HPS、HPS-NO_2树脂对水溶剂、环己烷溶剂中苯酚和苯胺吸附机理及性能。
A novel HPS-NO2 resin was prepared linked polystyrene resin. The HPS-NO2 resin was by nitro group-modifying the base macroporous hypercross- characterized using IR and elemental analysis. The content of carboxyl groups introduced on HPS-NO2 resin by oxidation reaction was determined by the exchange rate measurement. The specific surface area and pore structure parameters of the resin were determined by nitrogen adsorption-desorption method. The adsorption mechanism and behavior of HPS and HPS-NO2 on phenol and aniline in water and cyclohexane were investigated.
作者
黄小娟
龙宇
付玉丽
钟世华
HUANG Xiao-juan;LONG Yu;FU Yu-li;ZHONG Shi-hua(College of Chemistry and Chemical Engineering, Hunan Normal University, National & Local Joint Engineering Laboratory for New Petro-chemical Materials and Fine Utilization of Resources, Key Laboratory of fine resources and advanced materials of Hunan Province, Changsha 410081, China)
出处
《精细化工中间体》
CAS
2017年第6期37-42,共6页
Fine Chemical Intermediates
基金
湖南省发改委科研项目(湘财企指[2015]83号)
湖南省大学生创新创业教育基地(湘教通[2016]393号)
关键词
超高交联聚苯乙烯树脂
硝化修饰
吸附
hypercrosslinked polystyrene resin
nitrification modification
adsorption