摘要
Due to the excellent mechanical properties, good corrosion resistance, high biocompatibility and nickel- free character, the high nitrogen nickel-free austenitic stainless steel （HNASS） becomes an ideally alternative material for coronary stents. Stent implantation works in harsh blood environment after a balloon dilatation, i.e., the material is used in a corrosive environment with a permanent deforma- tion. The present study attempts to investigate effects of pre-straining on high-cycle fatigue behavior and corrosion fatigue behavior of HNASS in Hank＇s solution and the relevant mechanism for coronary stents application. It is found that higher pre-straining on HNASS results in higher strength and maintains almost same corrosion resistance. Fatigue limit of 0% HNASS is 550 MPa, while corrosion fatigue limit is 475 MPa. And improvement in fatigue limit of 20% and 35% pre-strained HNASS is in comparison with the 0% HNASS, while corrosion would undermine the fatigue behavior of HNASS. In a suitable range, the pre- straining had a beneficial effect on corrosion fatigue strength of HNASS, such as nearly 300 MPa improved with 20% cold deformation. This result provides a good reference for predicting the life of HNASS stent and as well its design.
Due to the excellent mechanical properties, good corrosion resistance, high biocompatibility and nickel- free character, the high nitrogen nickel-free austenitic stainless steel （HNASS） becomes an ideally alternative material for coronary stents. Stent implantation works in harsh blood environment after a balloon dilatation, i.e., the material is used in a corrosive environment with a permanent deforma- tion. The present study attempts to investigate effects of pre-straining on high-cycle fatigue behavior and corrosion fatigue behavior of HNASS in Hank＇s solution and the relevant mechanism for coronary stents application. It is found that higher pre-straining on HNASS results in higher strength and maintains almost same corrosion resistance. Fatigue limit of 0% HNASS is 550 MPa, while corrosion fatigue limit is 475 MPa. And improvement in fatigue limit of 20% and 35% pre-strained HNASS is in comparison with the 0% HNASS, while corrosion would undermine the fatigue behavior of HNASS. In a suitable range, the pre- straining had a beneficial effect on corrosion fatigue strength of HNASS, such as nearly 300 MPa improved with 20% cold deformation. This result provides a good reference for predicting the life of HNASS stent and as well its design.
基金
supported financially by the National Natural Science Foundation of China (No. 31370976)