摘要
Five types of KNO_3-NH_4VO_3-rare earth metal nitrate（K-V-rare earth metal） catalysts supported on a-porous alumina ceramic substrates were prepared by a coating method. All the catalysts were characterized by X-ray diffraction and thermogravimetry/differential scanning calorimetry. Catalytic activities were evaluated by a soot oxidation reaction using a temperature-programmed reaction system. The experimental results show that the addition of rare earth metal compound could obviously improve the catalytic activities of the K-V-based catalysts. The proper ratio of K-V-rare earth metal catalysts can not only lower the soot onset ignition temperature, but also quicken the soot oxidation rate. The crystalline phases formed by K, V, and rare earth metal are stable.
Five types of KNO_3-NH_4VO_3-rare earth metal nitrate（K-V-rare earth metal） catalysts supported on a-porous alumina ceramic substrates were prepared by a coating method. All the catalysts were characterized by X-ray diffraction and thermogravimetry/differential scanning calorimetry. Catalytic activities were evaluated by a soot oxidation reaction using a temperature-programmed reaction system. The experimental results show that the addition of rare earth metal compound could obviously improve the catalytic activities of the K-V-based catalysts. The proper ratio of K-V-rare earth metal catalysts can not only lower the soot onset ignition temperature, but also quicken the soot oxidation rate. The crystalline phases formed by K, V, and rare earth metal are stable.
基金
Funded by the National Natural Science Foundation of China(Nos.21606140,21776147,and 51373086)
the Science-Technology Program in Higher Education Institutions of Shandong Province,China(J11LD05)
the Qingdao Municipal Science and Technology Commission,China(13-1-4-154-jch)