Wear-resistance Performance of Spray-welding Coating by Plasma Weld-surfacing

Alloy powders including Ni60, WC, CrC, and TiC with different mass ratios were deposited on medium carbon low alloy steel by plasma welding. Through the experiments, the optimal alloy powder reinforcing cutter tool surface properties were discovered. The wear resistance properties were investigated on the impact abrasive wear tester. The experimental results show that in terms of microstructure, there exists the shape of herringbone, spider mesh, broken flower structures in coatings. In addition, fusion area of four specimens surfacing welding layer displays a large number of acicular martensite with a small amount of austenite. The coating mainly consists of Ni-Cr-Fe austenitic phase and the other precipitates. TiC density is smaller, its content is less in alloy powder, in the process of surfacing welding, TiC is melted fully, which is mainly distributed in surface layer and middle layer of hard facing layer. The content of TiC gradually reduces from surface layer of hard facing layer to the fusion area. Compared to TiC, the density of tungsten carbide and chromium carbide is larger, there exist tungsten carbide and chromium carbide particles, which are not completely melted near the fusion area. The micro-hardness presents gradient change from the fusion area to the surface layer of hard facing layer, and the hardness of the middle layer is slightly lower than that of the fusion area, and the hardness increases near the surface layer.

Alloy powders including Ni60, WC, Cr_3C_2, and TiC with different mass ratios were deposited on medium carbon low alloy steel by plasma welding. Through the experiments, the optimal alloy powder reinforcing cutter tool surface properties were discovered. The wear resistance properties were investigated on the impact abrasive wear tester. The experimental results show that in terms of microstructure, there exists the shape of herringbone, spider mesh, broken flower structures in coatings. In addition, fusion area of four specimens surfacing welding layer displays a large number of acicular martensite with a small amount of austenite. The coating mainly consists of Ni-Cr-Fe austenitic phase and the other precipitates. TiC density is smaller, its content is less in alloy powder, in the process of surfacing welding, TiC is melted fully, which is mainly distributed in surface layer and middle layer of hard facing layer. The content of TiC gradually reduces from surface layer of hard facing layer to the fusion area. Compared to TiC, the density of tungsten carbide and chromium carbide is larger, there exist tungsten carbide and chromium carbide particles, which are not completely melted near the fusion area. The micro-hardness presents gradient change from the fusion area to the surface layer of hard facing layer, and the hardness of the middle layer is slightly lower than that of the fusion area, and the hardness increases near the surface layer.