摘要
High quality epitaxial single phase（Ga_（0.96）Mn_（0.04））_2O_3 and Ga_2O_3 thin films have been prepared on sapphire substrates by using laser molecular b（eam）epitaxy（L-MBE）. X-ray diffraction results indicate that the thin films have the monoclinic structure with a 201 preferable orientation. Room temperature（RT） ferromagnetism appears and the magnetic properties of β-（Ga_（0.96）Mn_（0.04））_2O_3 thin film are enhanced compared with our previous works. Experiments as well as the first principle method are used to explain the role of Mn dopant on the structure and magnetic properties of the thin films. The ferromagnetic properties are explained based on the concentration of transition element and the defects in the thin films.
High quality epitaxial single phase（Ga_（0.96）Mn_（0.04））_2O_3 and Ga_2O_3 thin films have been prepared on sapphire substrates by using laser molecular b（eam）epitaxy（L-MBE）. X-ray diffraction results indicate that the thin films have the monoclinic structure with a 201 preferable orientation. Room temperature（RT） ferromagnetism appears and the magnetic properties of β-（Ga_（0.96）Mn_（0.04））_2O_3 thin film are enhanced compared with our previous works. Experiments as well as the first principle method are used to explain the role of Mn dopant on the structure and magnetic properties of the thin films. The ferromagnetic properties are explained based on the concentration of transition element and the defects in the thin films.
基金
Project supported by the National Natural Science Foundation of China(Nos.11404029,51572033,51172208)
the Fund of State Key Laboratory of Information Photonics and Optical Communications(BUPT)