摘要
Effects of calcium( Ca) and yttrium( Y) on microstructure and mechanical properties of high strain-rate rolled AZ91 D magnesium alloy were studied. High strain-rate rolling can improve the strength and plasticity of magnesium alloy sheets.Additions of Ca and Y into AZ91 D can refine grains and modify the size and the distribution of the precipitated phases. After solution treatment( 418 ℃ and 20 h) and high strain-rate rolling( heating at420 ℃ for 10 min firstly and then rolling from 10 mm to 2 mm in thickness via a single pass),the tensile strength of the AZ91 D-0. 2%Ca alloy was 1. 3% higher than that of the AZ91 D-0. 4 D%Y alloy,and the tensile strength of the AZ91 D-0. 2%Ca-0. 4%Y alloy was about 8. 3% and 6. 9% higher than those of the AZ91 D-0. 4%Y and the AZ91 D-0. 2%Ca alloys respectively.
Effects of calcium（ Ca） and yttrium（ Y） on microstructure and mechanical properties of high strain-rate rolled AZ91 D magnesium alloy were studied. High strain-rate rolling can improve the strength and plasticity of magnesium alloy sheets.Additions of Ca and Y into AZ91 D can refine grains and modify the size and the distribution of the precipitated phases. After solution treatment（ 418 ℃ and 20 h） and high strain-rate rolling（ heating at420 ℃ for 10 min firstly and then rolling from 10 mm to 2 mm in thickness via a single pass）,the tensile strength of the AZ91 D-0. 2%Ca alloy was 1. 3% higher than that of the AZ91 D-0. 4 D%Y alloy,and the tensile strength of the AZ91 D-0. 2%Ca-0. 4%Y alloy was about 8. 3% and 6. 9% higher than those of the AZ91 D-0. 4%Y and the AZ91 D-0. 2%Ca alloys respectively.
作者
沈言锦
SHEN Yanjin(Hunan Automobile Engineering Professional College, Zhuzhou 412001, China)
基金
Natural Science Foundation of Hunan Province,China(No.2017JJ5032)