摘要
Zero-valent iron（ZⅥ） was loaded on expanded graphite（EG） to produce a composite material（EG-ZⅥ） for efficient removal of hexavalent chromium（Cr（Ⅵ））. EG and EG-ZⅥ were characterized by X-ray diffraction（XRD）, scanning electron microscopy（SEM）,Fourier-transform infrared（FTIR） spectroscopy and Brunauer–Emmett–Teller（BET） analysis. EG-ZⅥ had a high specific surface area and contained sub-micron sized particles of zero-valent iron. Batch experiments were employed to evaluate the Cr（Ⅵ） removal performance. The results showed that the Cr（Ⅵ） removal rate was 98.80% for EG-ZⅥ,which was higher than that for both EG（10.00%） and ZⅥ（29.80%）. Furthermore, the removal rate of Cr（Ⅵ） by EG-ZⅥ showed little dependence on solution p H within a p H range of 1–9.Even at pH 11, a Cr（Ⅵ） removal rate of 62.44% was obtained after reaction for 1 hr. EG-ZⅥ could enhance the removal of Cr（Ⅵ） via chemical reduction and physical adsorption,respectively. X-ray photoelectron spectroscopy（XPS） was used to analyze the mechanisms of Cr（Ⅵ） removal, which indicated that the ZⅥ loaded on the surface was oxidized, and the removed Cr（Ⅵ） was immobilized via the formation of Cr（III） hydroxide and Cr（III）–Fe（III）hydroxide/oxyhydroxide on the surface of EG-ZⅥ.
Zero-valent iron（ZⅥ） was loaded on expanded graphite（EG） to produce a composite material（EG-ZⅥ） for efficient removal of hexavalent chromium（Cr（Ⅵ））. EG and EG-ZⅥ were characterized by X-ray diffraction（XRD）, scanning electron microscopy（SEM）,Fourier-transform infrared（FTIR） spectroscopy and Brunauer–Emmett–Teller（BET） analysis. EG-ZⅥ had a high specific surface area and contained sub-micron sized particles of zero-valent iron. Batch experiments were employed to evaluate the Cr（Ⅵ） removal performance. The results showed that the Cr（Ⅵ） removal rate was 98.80% for EG-ZⅥ,which was higher than that for both EG（10.00%） and ZⅥ（29.80%）. Furthermore, the removal rate of Cr（Ⅵ） by EG-ZⅥ showed little dependence on solution p H within a p H range of 1–9.Even at pH 11, a Cr（Ⅵ） removal rate of 62.44% was obtained after reaction for 1 hr. EG-ZⅥ could enhance the removal of Cr（Ⅵ） via chemical reduction and physical adsorption,respectively. X-ray photoelectron spectroscopy（XPS） was used to analyze the mechanisms of Cr（Ⅵ） removal, which indicated that the ZⅥ loaded on the surface was oxidized, and the removed Cr（Ⅵ） was immobilized via the formation of Cr（III） hydroxide and Cr（III）–Fe（III）hydroxide/oxyhydroxide on the surface of EG-ZⅥ.
基金
supported by the National Key Research and Development Program of China(No.2017YFD0801503)
the Fundamental Research Funds for the Central Universities(No.PYVZ1703)
the Higher Education and High-quality and World-class Universities(PY201606)