摘要
以QSn7-0.2合金为研究对象,以进给比、首轮压下比、退火温度为变量因素,建立了单因素试验表,研究了不同参数对QSn7-0.2合金的晶粒尺寸的影响,并对其晶粒尺寸存在差异性的原因进行了分析。结果表明,当进给比增大时,微观组织内平均晶粒度呈现先减小后增大的趋势;当首轮压下比增大时,组织内平均晶粒尺寸变化不明显;当退火温度升高时,合金的平均晶粒尺寸略有增大。
Effects of different processing parameters,such as feeding ratio,the first induction and annealing temperature on grain size in the QSn7.0-2 alloy were analyzed by the single factor experimental table.The origination of difference on grain size was described.The results show that the average grain size in the microstructure is decreased firstly and then increased with the feed ratio increase.However,the increase of first induction can be ignored to effects on grain size change.With increasing in annealing temperature,the average grain size is increased slightly.
作者
汤传尧
樊文欣
孔维静
Tang Chuanyao,Fan Wenxin,Kong Weijing(College of Mechanical Engineering, North University of Chin)
出处
《特种铸造及有色合金》
CAS
CSCD
北大核心
2018年第5期578-580,共3页
Special Casting & Nonferrous Alloys