摘要
Micro-nano structured Li Fe（1-x）MnxPO4/C（0≤x≤0.05）cathodes were prepared by spray drying,followed by calcination at 700°C.The spherical Li Fe（1-x）MnxPO4/C（0≤x≤0.05）particles with the size of 0.5 to5.0μm are composed of lots of nanoparticles of 20 to 30 nm,and have the well-developed interconnected pore structure.In contrast,when Mn doping content is 3 mol%（x=0.03）,the Li Fe（0.97）Mn（0.03）PO4/C demonstrates maximum specific surface area of 31.30 m^2/g,more uniform pore size and relatively better electrochemical performance.The initial discharge capacities are 161.59,157.04 and 153.13 m Ah/g at a discharge rate of 0.2,0.5 and 1 C,respectively.Meanwhile,the discharge capacity retentions are～100%after 120 cycles.The improved electrochemical performance should be attributed to higher specific surface,smaller polarization voltage,and a high Li~＋diffusion rate due to the micro-nano porous structure and lattice expansion produced by Mn doping.
Micro-nano structured Li Fe（1-x）MnxPO4/C（0≤x≤0.05）cathodes were prepared by spray drying,followed by calcination at 700°C.The spherical Li Fe（1-x）MnxPO4/C（0≤x≤0.05）particles with the size of 0.5 to5.0μm are composed of lots of nanoparticles of 20 to 30 nm,and have the well-developed interconnected pore structure.In contrast,when Mn doping content is 3 mol%（x=0.03）,the Li Fe（0.97）Mn（0.03）PO4/C demonstrates maximum specific surface area of 31.30 m^2/g,more uniform pore size and relatively better electrochemical performance.The initial discharge capacities are 161.59,157.04 and 153.13 m Ah/g at a discharge rate of 0.2,0.5 and 1 C,respectively.Meanwhile,the discharge capacity retentions are～100%after 120 cycles.The improved electrochemical performance should be attributed to higher specific surface,smaller polarization voltage,and a high Li~＋diffusion rate due to the micro-nano porous structure and lattice expansion produced by Mn doping.
基金
financially supported by the Department of Education of Liaoning Province of China