摘要
Calcium silicate hydrate（C-S-H） with Ca/Si ratio 1.0 was prepared via precipitation in solution and heated at various temperatures to investigate its dehydration behavior. The dehydration, structural collapse and recrystallization characteristics of C-S-H and its microstructural change during heating process were investigated by XRD, SEM, Raman and TG-DSC techniques. C-S-H gradually lost non-evaporable water upon heating, about 50% and 80% non-evaporable water was removed below 200 and 400 ℃, respectively, and the rest was removed up to about 1 000 ℃. At 400 ℃, dehydrated C-S-H exhibited the increasing disordering of calcium/silicon environment and the decreasing symmetrical bending vibration of Si-O-Si of Q^2 silicate chains. At 650 ℃ non-bridging oxygen atoms（O（non）） attached to silicon were almost removed, and significant structural change occurred, and at 815 ℃ C-S-H dehydrated to wollastonite.
Calcium silicate hydrate（C-S-H） with Ca/Si ratio 1.0 was prepared via precipitation in solution and heated at various temperatures to investigate its dehydration behavior. The dehydration, structural collapse and recrystallization characteristics of C-S-H and its microstructural change during heating process were investigated by XRD, SEM, Raman and TG-DSC techniques. C-S-H gradually lost non-evaporable water upon heating, about 50% and 80% non-evaporable water was removed below 200 and 400 ℃, respectively, and the rest was removed up to about 1 000 ℃. At 400 ℃, dehydrated C-S-H exhibited the increasing disordering of calcium/silicon environment and the decreasing symmetrical bending vibration of Si-O-Si of Q^2 silicate chains. At 650 ℃ non-bridging oxygen atoms（O（non）） attached to silicon were almost removed, and significant structural change occurred, and at 815 ℃ C-S-H dehydrated to wollastonite.
基金
Funded by National Key R&D Program of China(No.2017YFB0310001)
the National Natural Science Foundation of China(Nos.51772226,51272193,51072150)