摘要
采用同步液相法制备纳米Fe/Ni双金属来去除溶液中的U(Ⅵ),通过BET、SEM等方法对双金属材料进行表征分析,用批试验法研究n(Fe)/n(Ni)比、pH、初始铀浓度、反应时间和温度对去除U(Ⅵ)的影响。结果表明,铁镍双金属体系去除U(Ⅵ)的最佳pH为3.5,反应平衡时间为30min,25℃时的饱和吸附量为161.91mg/g。
Nanoscale Fe/Ni bimetal was prepared by synchronous liquid phase method to remove U（VI） from aqueous solution. Nanoscale Fe/Ni bimetal was characterized by BET and SEM. Effects of n（Fe）/n（Ni）, p H value, initial U（VI） concentration, adsorption time, and adsorption temperature on remove of U（VI） were investigated by batch test method. The results show that adsorption capacity is 161.91 mg/g at pH=3.5, adsorption time of 30 min, and adsorption temperature of 25℃.
作者
刘晴晴
李小燕
秦启凤
刘宸
张梓晗
刘学
陈玉洁
LIU Qing-qing;LI Xiao-yan;QIN Qi-feng;LIU Chen;ZHANG Zi-han;LIU Xue;CHEN Yu-jie(State Key Laboratory Breeding Base of Nuclear Resources and Environment, Ministry of Education, East China University of Technology, Nanchang 330013, China)
出处
《有色金属（冶炼部分）》
CAS
北大核心
2018年第7期74-78,共5页
Nonferrous Metals（Extractive Metallurgy)
基金
国家自然科学基金资助项目(11465002
11205030
41761090)
江西省自然科学基金项目(20171ACB2021)
核资源与环境国家重点实验室项目(NRE1608)
东华理工大学研究生创新项目(DHYC-2017011)
关键词
纳米铁镍双金属
铀
去除
吸附量
nanoscale Fe/Ni bimetal
uranium
removal
adsorption capacity