摘要
将多巴胺包覆的二氧化钛核壳纳米粒子(TiO_2@PDA)接枝于织物表面,部分填充织物缝隙,再通过浸轧法使氧化石墨烯均匀铺展在织物表面,最后用连二亚硫酸钠还原,得到还原氧化石墨烯复合织物。该织物具有良好的导电性能,初始电阻和10次水洗后电阻分别为10 kΩ,30 kΩ;同时具有良好的抗紫外线性能,UPF值为105.6。
The dopamine coated titanium dioxide nanoparticles （TiO2@PDA） are grafted onto the surface of polyester fabric and are used to partitially fill the fabric crevice. Graphene oxide attached to the fabric is evenly spread on the surface of the polyester fabric with the reduction of sodium dithionate. The ob- tained composite fabric has good conductivity of tO kΩ of intial resistance and 30 kΩ of resistance after 10 times laundrying. The anti-UV performance of the fabric is also good with UPF of 105.6.
作者
李满秋
张良苗
陈长
曹传祥
高彦峰
LI Man-qiu;ZHANG Liang-miao;CHEN Zhang;CAO Chuan-xiang;GAO Yan-feng(School of Materials Science and Technology, Shanghai University, Shanghai 200444, Chin)
出处
《印染》
北大核心
2018年第12期17-21,共5页
China Dyeing and Finishing
关键词
功能性整理
抗紫外线
石墨烯
多巴胺
TIO2
导电性
耐水洗性
涤纶
functional finishing
ultraviolet resistance
graphene
dopamine
TiO2
conductivity
washingdurability
polyester fabric