Foamed glass-ceramics doped with cerium oxide（CeO_2）were successfully prepared from high-titanium blast furnace slag by one-step sintering.The influence of CeO_2 addition（1.5wt%–3.5wt%）on the crystalline phases,microstructure,and properties of foamed glass-ceramics was studied.Results show that CeO_2 improves the stability of the glass phase and changes the two-dimensional crystallization mechanism into three-dimensional one.XRD analysis indicates the presence of Ca（Mg,Fe）Si_2O_6 and Ca（Ti,Mg,Al）（Si,Al）_2O_（6 ）in all sintered samples.Added with CeO_2,Ti CeO_4 precipitates,and crystallinity increases,leading to increased thickness of pore walls and uniform pores.The comprehensive properties of foamed glass-ceramics are better than that of samples without CeO_2.In particular,the sample added with a suitable amount of CeO_2（2.5wt%）exhibits bulk density that is similar to and compressive strength（14.9 MPa）that is more than twice of foamed glass-ceramics without CeO_2.
Foamed glass-ceramics doped with cerium oxide（CeO_2）were successfully prepared from high-titanium blast furnace slag by one-step sintering.The influence of CeO_2 addition（1.5wt%–3.5wt%）on the crystalline phases,microstructure,and properties of foamed glass-ceramics was studied.Results show that CeO_2 improves the stability of the glass phase and changes the two-dimensional crystallization mechanism into three-dimensional one.XRD analysis indicates the presence of Ca（Mg,Fe）Si_2O_6 and Ca（Ti,Mg,Al）（Si,Al）_2O_（6 ）in all sintered samples.Added with CeO_2,Ti CeO_4 precipitates,and crystallinity increases,leading to increased thickness of pore walls and uniform pores.The comprehensive properties of foamed glass-ceramics are better than that of samples without CeO_2.In particular,the sample added with a suitable amount of CeO_2（2.5wt%）exhibits bulk density that is similar to and compressive strength（14.9 MPa）that is more than twice of foamed glass-ceramics without CeO_2.
基金
the Science and Technology Support Projects of Sichuan (No.2014GZ0011)
the Industry Promotion Projects of Panzhihua in China (No.2013CY-C-2) for their financial support