摘要
The microstructure and mechanical properties of magnesium(Mg) alloys are significantly influenced by the casting process. In this paper, a comparative study on microstructure and mechanical properties at ambient and elevated temperatures of AZ91-2 wt.% Ca(AZX912) Mg alloy samples prepared by gravity casting(GC), squeeze casting(SC) and rheo-squeeze casting(RSC), respectively, was carried out. The results show that α-Mg grains in SC and RSC samples are significantly refined compared to the GC sample. The average secondary dendritic arm spacing of AZX912 alloy samples decreases in the order of GC, SC and RSC. As testing temperature increases from 25 °C to 200 °C, strength of AZX912 alloy samples is reduced, while their elongation is increased continuously. Compared to GC and SC processes, RSC process can improve the mechanical properties of AZX912 alloy at both ambient and elevated temperatures. The enhancement of mechanical properties of RSC sample over GC and SC samples mainly results from grain refinement in the as-cast microstructure of AZX912 alloy.
The microstructure and mechanical properties of magnesium （Mg） alloys are significantly influenced by the casting process. In this paper, a comparative study on microstructure and mechanical properties at ambient and elevated temperatures of AZ91-2wt.% Ca （AZX912） Mg alloy samples prepared by gravity casting （GC）, squeeze casting （SC） and rheo-squeeze casting （RSC）, respectively, was carried out. The results show that mMg grains in SC and RSC samples are significantly refined compared to the GC sample. The average secondary dendritic arm spacing of AZX912 alloy samples decreases in the order of GC, SC and RSC. As testing temperature increases from 25 ~C to 200 ~C, strength of AZX912 alloy samples is reduced, while their elongation is increased continuously. Compared to GC and SC processes, RSC process can improve the mechanical properties of AZX912 alloy at both ambient and elevated temperatures. The enhancement of mechanical properties of RSC sample over GC and SC samples mainly results from grain refinement in the as-cast microstructure of AZX912 alloy.
作者
xiao-yang chen
yang zhang
ya-lin lu
xiao-ping li
Xiao-yang Chen;Yang Zhang;Ya-lin Lu;Xiao-ping Li(Key lab of advanced Materials Design and Additive Manufacturing of Jiangsu Province,Jiangsu University of Technology,Changzhou 213001,China)
基金
financially supported by the National Natural Science Foundation of China(No.51601076)
the Natural Science Fund for Colleges and Universities in Jiangsu Province(No.16KJB430013,17KJA430005)